Hardness is an important mechanical property index, which can reflect the characteristics of elastic and plastic deformation of materials.
The sample preparation is simple, the sample is basically not destroyed, and it is close to non-destructive testing. It is easy to operate and fast to measure on specimens of different sizes and shapes, and there is a similar conversion relationship between hardness and strength. According to the hardness value, the approximate strength limit can be obtained. Hardness measurement is the standard. Harder objects of quasi-shape and size contact the surface of the material under a certain pressure to measure the resistance of the material in the process of deformation, which is called hardness test。
硬度是一个重要的力学性能指标，它能反映材料弹性和塑性变形的特性指标。
硬度测定时试样制备简单，试样基本不被破坏，接近无损检测，在不同尺寸与形状的试样上测定时，操作简便，测量速度快，并且硬度与强度之间有着相似的换算关系，根据硬度值能够得出近似的强度极限值；硬度测定是用标准形状和尺寸的较硬物体在一定压力下接触材料表面，测定材料在变形过程中表现出来的抗力，称为硬度测试。
本文由|上海沪杏光学http://www.shhx17.com/shhx17/com_pro.asp整里提供
用不同的载荷施加力的方法所得到的硬度是表现材料抵抗塑性变形的能力，肖氏硬度则表现了材料抵抗弹性变形的能力；日常中我们把载荷大于1kg测试力的称为宏观硬度，它主要用于较大的试件，希望通过硬度测试能够反映材料的宏观性能；载荷小于1kg测试力的称为微观硬度，它主要用于小而薄的试件，希望反映出微小领域内的材料性能，如显微组织的相硬度、材料的表面硬度。
显微硬度的测试原理基本和维氏硬度测试相同，所不同的是压头采用的是两对面夹角为136°;底面为正方形的正四棱锥金刚石压头和一径角为 ，横断角为 的金刚石锥形压头，即：克努普金刚石压头（入下图）。
显微硬度计和维氏硬度计所用的载荷分别为：1kg、2kg、3kg、5kg、10kg、20kg、30kg、50kg、100kg、120kg等，常用的为1kg、2kg、5kg、10kg、30kg、50kg。
载荷的大小主要取决于试件的厚度。测试的最终硬度是通过压痕单位面积上所能承受的载荷来表示的。将选定的固定实验力（载荷）压入试样表面，并经过规定的保持时间（保荷），然后卸除实验力（卸荷）后，在试样表面残留出一个底面为正方形的正四棱锥或克努普压痕，通过测微目镜测量其对角线的长度，得到压痕的面积，显微硬度值就是实验力与压痕表面积的比值。 [上图为正四棱锥金刚石压头]
更多硬度计技术资料可点击：http://www.shhx17.com/shhx17/news.asp
上海沪杏光学仪器有限公司主要生产和销售金相显微镜、偏光显微镜、体视显微镜、检测显微镜、维氏硬度计等光学设备。销售部热线： 021-20227929 18801751626
更多金相材料方面资料欢迎来电来函咨询，邮箱h20227930@163.com
上一篇：洛氏硬度计维修与常见故障解决方法
下一篇：维氏硬度的计算公式